项目 | 标准 | 测试条件 | 单位 | HR-751 | FR-751 | HG-751 | 751UV | 熔融指数 | ASTM D-1238 | 200 ℃ 1.2kg | g/10min | 9.64 | 1.26 | 1.62 | 1.11 | 密度 | ASTM D-792 | | g/cm3 | 1.05 | 1.04 | 1.07 | 1.05 | 拉伸强度 | ASTM D-638 | | Mpa | 44.14 | 42.17 | 43.69 | 41.04 | 断裂伸长率 | ASTM D-638 | | % | 139.67 | 34.61 | 22.16 | 30.44 | 弯曲强度 | ASTM D-790 | | Mpa | 57.35 | 65.2 | 63.8 | 61.4 | 弯曲摸量 | ASTM D-790 | | Mpa | 1838.52 | 2344.82 | 2382.91 | 2501.85 | 悬臂梁缺口冲击强度 | ASTM D-256 | 23 ℃ 3.2mm | J/M | 720 | 220 | 271 | 246 | 维卡软化点 | ASTM D-1528 | 50 ℃/h | ℃ | 115 | 110 | 105 | 96 | 热变形温度 | ASTM D-648 | 1.82Mpa | ℃ | 110 | 95 | 95 | 91 | 阻燃性能 | UL-94 | 3.2mm | Class | HB | V-O | HB | V-O | 特性 | | | | 耐高温 | 阻燃 | 高光 | 抗紫外线 |
|