项目 | 标准 | 测试条件 | 单位 | FR-907S | FR-807S | 6170 | 807S | 7510UV | 熔融指数 | ASTM D-1238 | 300 ℃ 1.2kg | g/10min | 28 | 25 | 25 | 22 | 18 | 密度 | ASTM D-792 | | g/cm3 | 1.1 | 1.05 | 1.05 | 1.06 | 1.05 | 拉伸强度 | ASTM D-638 | | Mpa | 55 | 70 | 61 | 64 | 60 | 断裂伸长率 | ASTM D-638 | | % | 30 | 26 | 27 | 28 | 25 | 弯曲强度 | ASTM D-790 | | Mpa | 80 | 110 | 86 | 88 | 87 | 弯曲摸量 | ASTM D-790 | | Mpa | 2200 | 2900 | 2189 | 2226 | 2222 | 悬臂梁缺口冲击强度 | ASTM D-256 | 23 ℃ 3.2mm | J/M | 700 | 990 | 807 | 1018 | 1100 | 维卡软化点 | ASTM D-1528 | 50 ℃/h | ℃ | 128 | 138 | 135 | 131 | 130 | 热变形温度 | ASTM D-648 | 1.82Mpa | ℃ | 125 | 134 | 130 | 126 | 125 | 阻燃性能 | UL-94 | 3.2mm | Class | V-O | V-O | HB | HB | HB | 特性 | | | | 阻燃,抗 漏电起恨 | 阻燃 | 抗应裂 | 透明,韧性 好耐冲击 | 抗紫外线 |
|